This document specifies the general principles of a method for determining the transient extensional viscosity of polymer melts. The procedure details the measurement of polymer melt specimens stretched uniaxially under conditions of constant strain rate and constant temperature.

The method is capable of measuring the transient extensional viscosity of polymer melts at Hencky strain rates typically in the range 0,01 s–1 to 1 s–1, at Hencky strains up to approximately 4 and at temperatures up to approximately 250 °C (see NOTEs 1 and 2). It is suitable for measuring transient extensional viscosity values typically in the range from approximately 104 Pa⋅s to 107 Pa⋅s (see NOTE 3).

NOTE 1   Hencky strains and strain rates are used (see Clause 3).

NOTE 2   Values of strain, strain rate and temperature outside these limiting values can be attained.

NOTE 3   The operating limit of an instrument, in terms of the lowest transient extensional viscosity values that can be measured, is due to a combination of factors, including the ability of the specimen to maintain its shape during testing and the resolution of the instrument.

Standard first page

Preview 

Вы можете ознакомиться с данным стандартом в нашей онлайн-библиотеке (OBP)

Общая информация

  • Текущий статус
     : Опубликовано
    Дата публикации
     : 2021-04
    Этап
    : Опубликование международного стандарта [60.60]
  • Версия
     : 2
  • Технический комитет :
    ISO/TC 61/SC 5
    ICS :
    83.080.01 
  • RSS обновления

Жизненный цикл

Появились вопросы?

Ознакомьтесь с FAQ

Работа с клиентами
+41 22 749 08 88

Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)

  2. Интернет-магазин
  3. Каталог стандартов
  4. МКС
  5. 83
  6. 83.080
  7. 83.080.01
  8. ISO 20965:2021